Brisa Distressed

Manila

535-3021
  • General
    • Application
      Interior Upholstery
    • Composition
      100% Polycarbonate Polyurethane Surface 65% Recycled Polyester, 35% Rayon Backing
    • Weight
      Approx. 8.9 oz. per square yard
      Approx. 300 grams per square metre
    • Thickness
      Approx. 0.95 Millimetres
    • Width
      54 Inches / 137 Centimetres
    • Repeat
      8"V x 10.5"H / 203mm V x 267mm H
  • Performance
    • Abrasion
      ASTM D4157 - 300,000 Double Rubs (Wyzenbeek)*
      BS EN ISO 12947-2 - 160,000 Rubs (Martindale)*
      *meets or exceeds
    • Adhesion of Coating
      ASTM D751
    • Air Permeability
      ASTM D737
    • Antibacterial
      Not applicable
    • Antimicrobial
      Not applicable
    • Antimildew
      Not applicable
    • Breaking Strength
      Not Applicable
    • Cold Crack
      Not Applicable
    • Hydrolysis
      16 Weeks
      ASTM D3690 SECT. 6.11 (Hydrolytic Stability)
      ISO 1419 Method C (Accelerated Ageing)
    • Dimensional Change
      ASTM D 3597
    • Seam Strength
      ASTM D751
    • Sound Absorption
      ASTM C423
    • Tear Strength
      ASTM D2261
    • Tensile Strength
      BS EN ISO 1421
  • Colorfastness
    • UV
      Not applicable
    • Light
      AATCC 16.3, 200 Hours, Grade 4
      ISO 105 B02, Grade 6
    • Crocking
      AATCC 8, Class 4-5 Wet & Dry
    • Sea (Salt) Water
      Not applicable
    • Chlorinated Water
      Not applicable
    • Perspiration
      Not applicable
  • Flammability

      • ASTM E84 (Adhered) - Class A
      • CA TB 117-2013 - Pass 
      • FMVSS 302 - Pass
      • NFPA 260 - Class 1
      • UFAC - Class 1
      • CA AB 2998


      These fabrics, when treated and/or used with other compatible furniture components, have been shown to perform under the fire test conditions of:

      • ASTM E84 (Unadhered)
      • BS 5852 Source 0, 1 & 5 (Cig, Match & Crib 5)
      • IMO FTPC Part 8
      • BS EN 1021 Parts 1 & 2